Synthesis of superconducting magnesium diboride objects

ABSTRACT

A process to produce magnesium diboride objects from boron objects with a similar form is presented. Boron objects are reacted with magnesium vapor at a predetermined time and temperature to form magnesium diboride objects having a morphology similar to the boron object&#39;s original morphology.

CROSS-REFERENCE TO RELATED PATENT APPLICATIONS

[0001] This patent application is a divisional of copending U.S. patent application Ser. No. 09/939,307, filed Aug. 24, 2001 which claims the benefit of U.S. Provisional Patent Application No. 60/269,095, filed Feb. 15, 2001.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

[0002] This invention was made in part with Government support under DOE Contract No. W-7405-Eng-82. The Government may have certain rights in this invention.

FIELD OF THE INVENTION

[0003] The present invention relates generally to superconductivity, and more particularly relates to a method of manufacturing superconducting magnesium diboride objects.

BACKGROUND OF THE INVENTION

[0004] The recent discovery of superconductivity in magnesium diboride (MgB₂) having a superconducting transition temperature (T_(c)) of approximately thirty nine degrees Kelvin (39K) introduced a new, simple binary intermetallic superconductor having three atoms per formula unit. MgB₂ has a T_(c) that is higher by almost a factor of two of any known non-oxide and non-C₆₀-based compound. Measurements of the boron isotope effect in MgB₂, which is an indication of the extent to which phonons mediate superconductivity, are consistent with the superconductivity being mediated via electron-photon coupling. Measurements of the upper critical field, H_(c2)(T), the thermodynamic critical field, H_(c)(T), and the critical current, J_(c), indicate that MgB₂ is a type-II superconductor with properties that are consistent with an intermetallic superconductor that has a T_(c) of approximately 40 K.

[0005] It is believed that MgB₂ forms via a process of diffusion of magnesium (Mg) vapor into boron grains. Superconducting wire, tape, and film can be used for research and applied purposes. For example, superconducting wire can be used for making superconducting magnets, fault-current limiters, and for power transmission. Films can be used to make Josephson junctions, SQUIDS (superconducting quantum interference devices), micro-electronic interconnects and other devices. The films can also be used to coat microwave cavities and other objects.

BRIEF SUMMARY OF THE INVENTION

[0006] It is an object of the instant invention to provide a method of manufacturing magnesium diboride wires, tapes, and films. It is a further object of the instant invention to provide a method of manufacturing magnesium diboride wire using boron filaments and films using boron films.

[0007] In view of the above objects, it is an object of the instant invention to provide a method of manufacturing magnesium diboride wire and films utilizing simple cost effective techniques.

[0008] In accordance with an embodiment of the instant invention, a method of manufacturing magnesium diboride wire or film comprises the steps of exposing boron filaments, tape, or film to Mg vapor for a predetermined time and temperature to form MgB₂ wire, tape or film, removing the formed MgB₂ wire, tape or film from the Mg vapor, and either quenching the MgB₂ wire, tape or film to near ambient temperatures or quenching the reaction vessel to near ambient temperatures and removing the MgB₂ wire, tape or film from the reaction vessel.

[0009] In accordance with an alternate embodiment of the instant invention, a method of manufacturing magnesium diboride wire, tape or film comprises the steps of: a) sealing at least one boron filament, tape or film and magnesium into a tantalum (Ta) or similarly inert tube with excess magnesium with respect to MgB₂; b) protecting the tantalum from oxidation (e.g., sealing the Ta tube in quartz) ; c) heating the sealed Ta tube at 950 C. for two hours or less for a boron filament diameter of 100 micrometers (with differing heating times and temperatures for differing thicknesses of boron used); d) quenching the Ta tube to room temperature and removing the formed magnesium diboride wire, tape or film from the Ta

[0010] Other objectives and advantages of the invention will become more apparent from the following detailed description when taken in conjunction with the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

[0011] The accompanying drawings incorporated in and forming a part of the specification illustrate several aspects of the present invention, and together with the description serve to explain the principles of the invention. In the drawings:

[0012]FIG. 1a is a flow diagram for illustrating a methodology for manufacturing magnesium diboride wire;

[0013]FIG. 1b is a flow diagram for illustrating an alternate methodology for manufacturing magnesium diboride wire;

[0014]FIG. 2a is a cross-sectional view of a boron filament used in the manufacturing of magnesium diboride wire;

[0015]FIG. 2b is a cross-sectional view of magnesium diboride wire made in accordance with the teachings of the instant invention;

[0016]FIG. 3 is an image of magnesium diboride wires made in accordance with the teachings of the instant invention;

[0017]FIG. 4 is a graphic illustration of the magnetization divided by an applied magnetic field of 25 Oe for a zero field cooled magnesium diboride wire made in accordance with the teachings of the instant invention;

[0018]FIG. 5 is a graphical plot illustrating the relationship between the electrical resistivity of magnesium diboride wire and temperature;

[0019]FIG. 6 is an expanded view of the resistivity data of FIG. 5 near the superconducting transition temperature; and

[0020]FIG. 7 is a graphic illustration of H_(c2)(T) data inferred from the resistivity data similar to that shown in FIG. 5; and

[0021]FIG. 8 is a graphic illustration of the superconducting critical current density as a function of an applied field for temperatures ranging from 5K to 35K in increments of 5K.

[0022] While the invention will be described in connection with certain preferred embodiments, there is no intent to limit it to those embodiments. On the contrary, the intent is to cover all alternatives, modifications and equivalents as included within the spirit and scope of the invention as defined by the appended claims.

DETAILED DESCRIPTION OF THE INVENTION

[0023] While the instant invention may be used to manufacture magnesium diboride (MgB₂) objects such as MgB₂ wire, tape, and film, the instant invention will be described using MgB₂ wire. Those skilled in the art will recognize that the process used to make the MgB₂ wire can also be used to make MgB₂ film, tape or any other form or structure by turning boron having a similar morphology (i.e., form) into MgB₂ via exposure to magnesium vapor. For example, boron coatings on cavities or other devices could be turned into MgB₂ coatings. Turning now to FIG. 1a, the steps to manufacture magnesium diboride (MgB₂) wire are shown. Boron filaments are fed into a reaction chamber or vessel (step 100). The boron filaments may be continually fed into the reaction vessel or pre-cut to a specified length. The boron filaments are exposed to Mg vapor in the reaction vessel for a predetermined time and temperature to form MgB₂ wire (step 102). The vapor pressure is determined by the reaction vessel temperature using well established vapor pressure versus temperature curves as known in the art. The minimum exposure time increases with increasing filament diameter and decreases with increasing temperature. For example, a 100 micrometer diameter boron filament that is exposed to Mg vapor heated to or near 950 C. for approximately two hours forms MgB₂ wire. A 140, 200, or 300 micrometer diameter filament must be heated longer than two hours for the transformation to be completed. The 140 and 200 micrometer diameter filaments form wire when exposed to Mg vapor heated to or near 950 C. for near 6 hours and the 300 micrometer diameter filaments form wire when exposed to Mg vapor heated to or near 950 C. for near 15 hours. During the heating step, MgB₂ wire is formed as a result of the reaction between the boron filaments and the Mg vapor. After the MgB₂ wire has been formed, the MgB₂ wire is removed from the reaction vessel (step 104). The MgB₂ wire is quenched to near ambient temperatures or is cooled at a predetermined ramp rate.

[0024] The same process is used for other boron objects. For example, MgB₂ films are created by depositing boron film on a substrate inert to the Mg vapor such as strontium titanate. The film is deposited using pulsed laser deposition or other known methods of deposition. Once the boron film is deposited on the substrate, the film is placed or fed into a reaction vessel and exposed to Mg vapor for a predetermined time and temperature. For example, a one micrometer thick boron film that is exposed to Mg vapor heated to or near 950 C. for approximately a half hour forms MgB₂ film. After the MgB₂ film is formed, the film is removed from the reaction vessel and either quenched to near ambient temperature or is cooled at a predetermined ramp rate.

[0025] Turning now to FIG. 1b, the steps to manufacture magnesium diboride (MgB₂) wire using an alternate embodiment are shown. Boron filaments and magnesium are placed into a tantalum (Ta) or other inert tube such as niobium, molybdenum, tungsten, and possibly iron and some steels (step 110). The nominal ratio of magnesium to boride in the Ta tube is Mg₂B. While a nominal ratio of Mg₂B was used, those skilled in the art will recognize that other ratios may be used provided that there is excess magnesium with respect to MgB₂ (i.e., the ratio of Mg:B is greater than 1:2). The Ta tube is then sealed in quartz or an equivalent material to protect the Ta from oxidation at elevated temperatures (step 112). Those skilled in the art will recognize that other methods of providing such protection can be used. The sealed Ta tube is placed in a box furnace at a temperature of 950 C. for approximately two hours (step 114). The Ta tube is then removed and cooled to room temperature (step 116). MgB₂ wire forms during the temperature soak at 950 C. and the wire is removed when the Ta tube is near room ambient temperature (step 118).

[0026] Now that the manufacturing processes have been described, the characteristics of the MgB₂ wire formed will now be described. Turning now to FIGS. 2a and 2 b, the boron filament 200 and MgB₂ wire 210 are shown. In FIG. 2a, a cross-section of a boron filament 200 is shown. The boron filament diameter 202 is 100 μm and it has a tungsten/tungsten boride core 204 having a diameter of approximately 15 μm. The tungsten/tungsten boride core 204 is part of the boron filament 200 and does not appear to be effected by the exposure of the boron filament 200 to magnesium. As discussed hereinbelow, the tungsten/tungsten boride core 204 does not seem to effect the superconducting properties of the resulting MgB₂ wire. While a 100 μm diameter filament was used, it should be recognized that other diameters and boron tapes may be used with appropriate changes in temperature and time of exposure to Mg vapor. FIG. 2b shows a cross-section of MgB₂ wire 210 produced after steps 100-104 or 110-118 are taken. In FIG. 2b, the MgB₂ wire 210 has a diameter 212 of approximately 160 μm. The increased diameter of the MgB₂ wire 210 is consistent with observations that there is an expansion associated with the formation of MgB₂ powders during synthesis.

[0027]FIG. 3 shows an image of the resulting MgB₂ wire segments 300. As can be seen, there has been significant warping and bending of the boron filament 200 as a result of the reaction with the magnesium vapor at high temperature. Although the MgB₂ wire segments 300 are somewhat brittle, the integrity of the filament segments is preserved during the exposure to the Mg vapor (i.e. the boron filaments 200 do not decompose or turn into powder). The MgB₂ wire may be encased in a sleeve to increase mechanical stability of the MgB₂ wire.

[0028] Based upon a diameter 212 of 160 μm and measuring the length and mass of several MgB₂ wire segments 300, the density of the wire is determined to be approximately 2.4 g/cm³. This is to be compared with a theoretical value of 2.55 g/cm³ for a single crystal sample using lattice parameters a=3.14 Å and c=3.52 Å for the hexagonal unit cell. This implies that the MgB₂ wire segments 300 are probably better than approximately 90% of the theoretical density. It should be noted that the small tungsten/tungsten boride core would come in as a roughly 10% correction, and therefore is within the level of uncertainty.

[0029] Turning now to FIG. 4, the temperature-dependent magnetization of MgB₂ wire is shown. The data were taken after the MgB₂ wire segments 300 were cooled in a zero magnetic field and then warmed in a field of 25 Oe (Oersteds). Taking into account the aspect ratio of the MgB₂ wire segments, a susceptibility very close to a value of −¼π, which is the value expected for total shielding and a demagnetization factor close to zero, was obtained. The superconducting transition temperature (T_(c)) of 39.4 K is determined from these data by using an onset criterion (2% of −¼π). The width of the temperature transition (10%-90%) is 0.9 K.

[0030] Turning now to FIG. 5, the temperature-dependent electrical resistivity of MgB₂ wire segments 300 formed by the process of the present invention is shown. The resistivity, ρ, at room temperature has a value of 9.6 μOhm-cm whereas ρ at 77 Kelvin has a value of 0.6 μOhm-cm and ρ at 40 Kelvin has a value of 0.38 μOhm-cm. This leads to a residual resistivity ratio of RRR equal to 25.3. The resistivity for temperatures just above T_(c) is lower by a factor of ten to twenty over existing superconducting materials such as Nb₃Sn. This means that the MgB₂ wire may manifest less need to be encased in a relatively higher conducting sleeve (such as copper) as required by materials such as Nb₃Sn to keep wire resistance down in the event that temperature rises above the superconducting transition temperature of the material being used. It should be noted that the shape of the resistivity curve and the RRR values are qualitatively the same as the shape and RRR values observed for sintered pellets of polycrystalline Mg¹⁰B₂. The resistivity of the sintered pellet samples of polycrystalline Mg¹⁰B₂ is approximately 1 μOhm-cm at 40 K. This somewhat higher value of the calculated resistivity for the sintered pellet samples of polycrystalline Mg¹⁰B₂ is consistent with the sintered pellet sample having an actual density substantially lower than either the MgB₂ wire or the theoretical value.

[0031] The temperature-dependent resistivity shown in FIG. 5 can be fit by a power law of ρ=ρ₀+ρ₁T^(α) with α approximately equal to 2.6 between the superconducting critical temperature, T_(c), and 200 Kelvin. This is comparable to the power law R=R₁+R₁T^(α1), with α₁ approximately equal to 2.8, found for the sintered Mg¹⁰B₂ pellet samples over a comparable temperature range. Due to the similarity of the two power laws, those skilled in the art will recognize that that the resistivity of MgB₂ will not have a linear slope for temperatures between T_(c) and 300 Kelvin. On the other hand, using an average Fermi velocity of ν_(F)=4.8·10⁷ cm/s and a carrier density of 6.7·10²² el/cm³ (two free electrons per unit cell) the electronic mean free path is estimated to be approximately 600 Å at T_(c). This is clearly an approximate value of the electronic mean free path, but with an estimated superconducting coherence length of approximately 50 Å, these values place MgB₂ wire segments 300 well within the clean limit, which those skilled in the art will recognize as a indication of high sample quality. This indicates that superconducting properties such as the upper critical field and critical current may be improved by the judicious addition of impurities.

[0032] The superconducting transition temperature, T_(c)=39.4 K, can be determined from both the magnetization and resistivity data shown in FIGS. 4 and 5. This value is slightly higher than the T_(c)=39.2 K value determined for isotopically pure Mgl B₂, but is significantly lower that T_(c)=40.2 K for Mg¹⁰B₂. The value is consistent with an approximate 80% natural abundance of ¹¹B. It should be noted that the superconducting transition is both relatively high and sharp in the MgB₂ wire segments 300. This means that either very few impurities are being incorporated into the MgB₂ wire segments 300 or that what few impurities are being incorporated are having very little effect on either resistivity or T_(c). FIG. 6 shows an expanded view of the temperature-dependent resistivity data of FIG. 5 near the superconducting transition temperature T_(c).

[0033] The temperature dependence of the upper critical field, H_(c2)(T), is illustrated in FIG. 7. For each field, three data points are shown. The three data points are onset temperature, temperature for maximum dρ/dT, and completion temperature. Qualitatively these data are similar to the H_(c2)(T) data inferred from measurements on Mg¹⁰B₂ sintered pellets. Quantitatively, at an H of 9 T, the width of the resistive transition for a MgB₂ wire segments 300 is roughly half of the width found for the sintered Mg¹⁰B₂ pellet samples. These data are consistent with the wire sample being of comparable or better quality as the sintered pellet samples.

[0034] Turning now to FIG. 8, data on the critical current J_(c) is shown. The open symbols, represented generally as 400, are J_(c) values extracted from direct measurements of the current dependent voltage across the MgB₂ wire segment 300 at given temperature and applied field values. The filled symbols, represented generally as 402, are J_(c) values inferred from magnetization loops by application of the Bean model. The temperature values are incremented every 5K and range from 5K to 35K. 5K measurements and extrapolations are generally illustrated at line 404, 10K measurements and extrapolations are generally illustrated at line 406, 15K measurements and extrapolations are generally illustrated at line 408, 20K measurements and extrapolations are generally illustrated at line 410, 25K measurements and extrapolations are generally illustrated at line 412, 30K measurements and extrapolations are generally illustrated at line 414, and 35K measurements and extrapolations are generally illustrated at line 416. The dashed lines connect data sets taken at the same temperature. The direct measurement of J_(c) was limited to values below approximately 200 A/cm² due to resistive heating from the leads attached to the MgB₂ wire segment 300 and contact resistance. As can be seen, the extrapolations of the directly measured, low J_(c), data and the Bean-model-inferred, high J_(c), data match up moderately well. In comparison to the J_(c) data for a sintered pellet of Mg¹⁰B₂, _(c) for the MgB₂ wire segment 300 is roughly a factor of two higher at low fields and temperatures and over an order of magnitude higher at high fields.

[0035] A simple technique of producing low resistivity, high density, high T_(c) MgB₂ in wire, tape, or film form via exposure of boron filaments, tape, or film to Mg vapor has been presented. The resulting MgB₂ wire has approximately 90% the theoretical density of MgB₂ and measurements of the temperature dependent resistivity reveal that MgB₂ is highly conducting in the normal state. The room temperature resistivity has a value of 9.6 μOhm-cm whereas the resistivity at a temperature of 40 K is 0.38 μOhm-cm. This means that even in the normal state, MgB₂ wires can carry significant current densities. This should be compared with the resistivity of Nb₃Sn, which has a resistivity value of 11 μOhm-cm at a temperature of 20K and a resistivity value of 80 μOhm-cm at a temperature of 300 K.

[0036] The MgB₂ wires can be used for both research and applied purposes. Examples include, but are not limited to, superconducting magnets, power transmission lines, fault-current limiters, and micro-electronic circuits (e.g. SQUIDS or interconnects). It should be noted that boron filaments and tapes are produced in a variety of sizes and of arbitrary lengths and that different applications may require different sizes of MgB₂ wires or tapes. The conversion of boron filaments or tapes into MgB₂ wire or tapes as part of a continuous process leads to the possibility of simple manufacturing of light weight, high T_(c), wires or tapes with remarkably small normal state resistivities. Additionally, the process used in creating the MgB₂ wire or tape can be used to turn boron coatings on cavities or other devices into high-quality superconducting films.

[0037] The foregoing description of various embodiments of the invention has been presented for purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise embodiments disclosed. Numerous modifications or variations are possible in light of the above teachings. The embodiments discussed were chosen and described to provide the best illustration of the principles of the invention and its practical application to thereby enable one of ordinary skill in the art to utilize the invention in various embodiments and with various modifications as are suited to the particular use contemplated. All such modifications and variations are within the scope of the invention as determined by the appended claims when interpreted in accordance with the breadth to which they are fairly, legally, and equitably entitled. 

What is claimed is:
 1. A magnesium diboride wire formed by the step comprising exposing a boron filament to magnesium vapor in a reaction vessel for a predetermined time and temperature.
 2. The magnesium diboride wire of claim 1 wherein a ratio of magnesium to boron is in excess of 1:2.
 3. The magnesium diboride wire of claim 1 wherein the boron filament has a core comprised of a core material that is inert to magnesium vapor.
 4. The magnesium diboride wire of claim 1 wherein the core material is tungsten/tungsten boride.
 5. The magnesium diboride wire of claim 1 further comprising a conductive sleeve encasing the formed magnesium diboride wire.
 6. A magnesium diboride film formed by the steps comprising: putting a boron film and magnesium into an inert tube; heating the inert tube to a predetermined temperature for a predetermined time to form the magnesium diboride film; cooling the magnesium diboride film at a predetermined rate; and removing the formed magnesium diboride film from the inert tube.
 7. The magnesium diboride film of claim 6 wherein the boron film is deposited on a substrate that is inert to the magnesium. 